Irradiation embrittlement is a problematic issue for internal structures, such as acore shroud, in a light water reactor. It is characterized by decreased ductility andtoughness, and increased yield strength and hardening due to increased dislocations.Before this thesis a core shroud from a BWR was cut into pieces based on the estimatedneutron damage on the welds. Two of the pieces cut out was used in this thesis, A2( 0.5dpa) and C2(<0.1 dpa). In this thesis Vickers hardness tests and uniaxial tensile testswere used to give an estimation of the embrittlement of the welds. An estimation ofyield strength of A2 was also calculated based on the resulting hardness. The Vickerstests showed noticeable hardening in the weld, both at 0.1 dpa and 0.5 dpa. The ATTalso showed an increase in yield strength in C2. The calculated yield strength alsoshowed an increase. In conclusion, the core shroud has a decreased toughness, henceincreased risk of unexpected brittle fracture.

Bestrålningsförsprödning är ett rådande problem för interna strukturer, såsom enmoderatortank, i lättvattenreaktorer. Den kännetecknas av minskad duktilitet ochseghet, och ökad sträckgräns och härdning på grund av ökade dislokationer. Föredetta examensarbete skars en moderatortank från en BWR i bitar baserat på denuppskattade neutronskadan på svetsarna. Två av de utskurna bitarna användes idenna avhandling, A2( 0,5 dpa) och C2(<0,1 dpa). I detta arbete användes Vickershårdhetstester och dragprover för att ge en uppskattning av svetsarnas sprödhet. Enuppskattning av sträckgränsen för A2 beräknades också baserat på den resulterandehårdheten. Vickers-testerna visade märkbar härdning i svetsen, både vid 0,1 dpaoch 0,5 dpa. ATT visade också en ökning av sträckgränsen i C2. Den beräknadesträckgränsen visade också en ökning. Sammanfattningsvis har moderatortanken enminskad seghet, därav ökad risk för oväntad spröd fraktur.