Low temperature creep crack growth in low alloy reactor pressure vessel steel
KTH, Skolan för industriell teknik och management (ITM), Materialvetenskap, Materialteknologi.ORCID-id: 0000-0002-8494-3983
2005 (Engelska)Ingår i: Journal of Nuclear Materials, ISSN 0022-3115, E-ISSN 1873-4820, Vol. 336, nr 03-feb, s. 279-290Artikel i tidskrift (Refereegranskat) Published
Abstract [en]

Uni-axial creep and creep crack growth (CCG) tests between 320degreesC and 420degreesC have been carried out in a low alloy reactor pressure vessel steel (ASTM A508 class 2). Both as-received material and simulated coarse grained heat affected zone (CGHAZ) microstructure have been tested. CCG does occur at tested temperatures. The lifetimes for the CCG tests are considerably shorter than those for the uni-axial creep tests at the same reference stress and temperature. This is more pronounced at longer lifetimes or lower stresses. Increasing temperature causes a significant reduction of lifetime, e.g. the CCG lifetime on the simulated CGHAZ is reduced by a factor of five as temperature raises from 320degreesC to 340degreesC at given reference stresses. Three distinct regions relating crack length and time are observed for the CCG tests. After incubation, the crack grows steadily until it accelerates to approach failure. For the longer time CCG tests, the cracks propagate intergranularly, independent of temperature and microstructure. An approximate linear extrapolation based on the stress-time results indicates that the reference stress causing failure in the simulated CGHAZ due to CCG at a given lifetime of 100 000 h at 320 degreesC is lower than both yield and tensile strengths, showing that the design stress should be based on creep crack growth property rather than static strength.

Ort, förlag, år, upplaga, sidor
2005. Vol. 336, nr 03-feb, s. 279-290
Nyckelord [en]
c-mn steel, potential method, 360-degrees-c
Identifikatorer
URN: urn:nbn:se:kth:diva-14509DOI: 10.1016/j.jnucmat.2004.10.001ISI: 000226817700019OAI: oai:DiVA.org:kth-14509DiVA, id: diva2:332550
Anmärkning
QC 20100525Tillgänglig från: 2010-08-05 Skapad: 2010-08-05 Senast uppdaterad: 2017-12-12Bibliografiskt granskad

Open Access i DiVA

Fulltext saknas i DiVA

Övriga länkar

Förlagets fulltext

Personposter BETA

Sandström, Rolf

Sök vidare i DiVA

Av författaren/redaktören
Sandström, Rolf
Av organisationen
Materialteknologi
I samma tidskrift
Journal of Nuclear Materials

Sök vidare utanför DiVA

GoogleGoogle Scholar

doi
urn-nbn

Altmetricpoäng

doi
urn-nbn
Totalt: 64 träffar
RefereraExporteraLänk till posten
Permanent länk

Direktlänk
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annat format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annat språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf