Effects of the presence of compression in transverse cyclic loading on fibre-matrix debonding in unidirectional composite plies
KTH, Skolan för teknikvetenskap (SCI), Hållfasthetslära (Inst.).
2007 (Engelska)Ingår i: Composites. Part A, Applied science and manufacturing, ISSN 1359-835X, E-ISSN 1878-5840, Vol. 38, nr 11, s. 2260-2269Artikel i tidskrift (Refereegranskat) Published
Abstract [en]

Fatigue of composite materials is of great concern in load-carrying structures. The first type of damage to appear is generally transverse cracks in off-axis plies. These cracks form when fibre-matrix debonds coalesce. The underlying mechanism is hence fatigue growth of debonds at the fibre-matrix interfaces. In the present study, debond growth has been characterized under tensile and compressive cyclic loading of single glass fibres embedded in polymer matrix. The debond length was deter-mined by in situ microscopy with transmitted polarized light showing the more damaging effect of tension-compression cyclic loading than tension-tension cyclic loading. A boundary element model has been developed and interfacial fracture mechanics concepts applied over the numerical results aiming to give an explanation of this experimental fact. These results may be used to formulate a fatigue growth law at a local microscopic level, at a stage prior to the formation of any visible damage, i.e. transverse cracks. Ideas of how to develop this methodology further are also discussed.

Ort, förlag, år, upplaga, sidor
2007. Vol. 38, nr 11, s. 2260-2269
Nyckelord [en]
fatigue, debonding, micro-mechanics, tension-compression cyclic loading, interface crack, fatigue, failure, delamination, prediction, friction
Nationell ämneskategori
Teknisk mekanik
Identifikatorer
URN: urn:nbn:se:kth:diva-17164DOI: 10.1016/j.compositesa.2006.11.002ISI: 000251657400003Scopus ID: 2-s2.0-35549009750OAI: oai:DiVA.org:kth-17164DiVA, id: diva2:335207
Anmärkning
3rd International Conference on Composites Testing and Model Identification Location: Univ Porto, Oporto, Portugal, Date: APR 10-12, 2006Tillgänglig från: 2010-08-05 Skapad: 2010-08-05 Senast uppdaterad: 2017-12-12Bibliografiskt granskad

Open Access i DiVA

Fulltext saknas i DiVA

Övriga länkar

Förlagets fulltextScopus

Sök vidare i DiVA

Av författaren/redaktören
Gamstedt, E. Kristofer
Av organisationen
Hållfasthetslära (Inst.)
I samma tidskrift
Composites. Part A, Applied science and manufacturing
Teknisk mekanik

Sök vidare utanför DiVA

GoogleGoogle Scholar

doi
urn-nbn

Altmetricpoäng

doi
urn-nbn
Totalt: 95 träffar
RefereraExporteraLänk till posten
Permanent länk

Direktlänk
Referera
Referensformat
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annat format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annat språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf