Ändra sökning
RefereraExporteraLänk till posten
Permanent länk

Direktlänk
Referera
Referensformat
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annat format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annat språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf
Long-term performance of a polyamide-12-based fuel line with a thin poly(ethylene-co-tetrafluoroethylene) (ETFE) inner layer exposed to bio- and petroleum diesel
KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
Visa övriga samt affilieringar
2018 (Engelska)Ingår i: Polymer degradation and stability, ISSN 0141-3910, E-ISSN 1873-2321, Vol. 156, s. 170-179Artikel i tidskrift (Refereegranskat) Published
Abstract [en]

The long-term performance of a polyamide-12 (PA12)-based (bio)diesel fuel line/pipe with a thin poly(ethylene-co-tetrafluoroethylene) (ETFE) inner layer was investigated in “close to real” and high-temperature isothermal conditions with fuel on the inside and air on the outside of the pipe. The inner carbon-black-containing ETFE layer resisted fuel attack, as revealed by the small fuel uptake, the very low degree of oxidation, and the unchanged electrical conductivity, glass transition and melting behaviour. The properties of the ETFE layer remained the same after exposure to all the fuel types tested (petroleum diesel, biodiesel and a blend of 80% diesel with 20% biodiesel). Because of the presence of the ETFE layer on the inside, the fuel pipe experienced noticeable changes only in the outer PA12 pipe layer through migration of plasticizer, annealing and slight oxidation. The evaporation of plasticizer was found to be diffusion-controlled and it led to an increase in the glass transition temperature of PA12 by 20 °C. This, together with a small annealing-induced increase in crystallinity, resulted in a stiffer and stronger pipe with an increase in the flexural/tensile modulus and strength. The oxidation of PA12 remained at a low level and did not lead to an embrittled pipe during the simulated lifetime of the vehicle. This study reveals that fluoropolymers have a great potential for use as fuel-contacting materials in “demanding” motor vehicle fuel line systems. 

Ort, förlag, år, upplaga, sidor
Elsevier Ltd , 2018. Vol. 156, s. 170-179
Nyckelord [en]
Ageing, Biodiesel, Diesel, Fuel pipe, Plasticizer loss, Poly(ethylene-co-tetrafluoroethylene), Polyamide, Carbon black, Diesel fuels, Ethylene, Fluorine containing polymers, Gasoline, Glass, Oxidation, Plasticizers, Polyamides, Reinforced plastics, Electrical conductivity, Fuel pipes, High temperature, Isothermal conditions, Long term performance, Tetrafluoroethylene, Glass transition
Nationell ämneskategori
Naturresursteknik
Identifikatorer
URN: urn:nbn:se:kth:diva-236649DOI: 10.1016/j.polymdegradstab.2018.09.003ISI: 000448091400017Scopus ID: 2-s2.0-85053044298OAI: oai:DiVA.org:kth-236649DiVA, id: diva2:1262851
Forskningsfinansiär
Energimyndigheten, 32519-3
Anmärkning

Export Date: 22 October 2018; Article; CODEN: PDSTD; Correspondence Address: Wei, X.-F.; KTH Royal Institute of Technology, School of Engineering Sciences in Chemistry, Biotechnology and Health, Fibre and Polymer TechnologySweden; email: xinfengw@kth.se; Funding details: 32519-3; Funding text: The financial support from the Swedish Energy Authority (project no. 32519-3 ), Volvo Cars AB (Göteborg, Sweden) and Scania CV AB (Södertälje, Sweden) is gratefully acknowledged. QC 20181113

Tillgänglig från: 2018-11-13 Skapad: 2018-11-13 Senast uppdaterad: 2019-09-30Bibliografiskt granskad
Ingår i avhandling
1. Ageing behavior of plastics used in automotive fuel systems
Öppna denna publikation i ny flik eller fönster >>Ageing behavior of plastics used in automotive fuel systems
2019 (Engelska)Doktorsavhandling, sammanläggning (Övrigt vetenskapligt)
Abstract [en]

The increase in service temperature and the use of biobased fuels, such as biodiesel, have raised concerns on the short/long-term performance of plastic components used in automotive fuel systems.

In this work the ageing behavior of unreinforced and glass-fibre reinforced polyamide 12 (PA12), exposed to three different fuels (petroleum diesel, biodiesel, and a mixture of these (80/20)) at high temperature, was investigated. The interactions between the polymer and the fuel, and the associated polymer ageing mechanisms (fuel uptake, extraction of monomer and oligomers, annealing and oxidation), were found to be “generic” in the sense that they occurred, although to various extent, for all fuels. In the glass-fibre reinforced polyamides, the ageing occurred mainly in the polyamide matrix and not in the matrix-fibre interface. The semi-aromatic polyamide showed better performance when exposed to fuels than the aliphatic PA12.  

At a component level, multilayer polyamide-based pipes, with polyamide or fluoropolymer as inner layer, were aged under “in-vehicle” conditions where the pipes were exposed to fuel on the inside and to the air on the outside. All pipes stiffened during ageing but embrittlement occurred only for the pipes with polyamide being the inner layer. Compared to polyamide, the fluoropolymer inner layer showed significantly better barrier properties towards the fuel and no material was extracted into the fuel. The plasticizer loss from the PA12 outer layers into air was diffusion controlled and its diffusivity followed a linear Arrhenius behavior in the high temperature region. Relationships between plasticizer loss and the changes in mechanical properties were established.

The polyamides experienced diffusion-limited oxidation when exposed to air and/or fuel, involving the formation of a thin oxidized surface layer which was responsible for a significant decrease in strain-at-break. 

The fracture behavior of PA 6 in air at high temperature, found to involve three distinct stages, were systematically studied and linked to underlying mechanisms responsible for the reduction in strain-at-break.

Abstract [sv]

En ökning i servicetemperatur och användning av biobaserade drivmedel, t.ex. biodiesel, har väckt frågeställningar om hur detta påverkar egenskaperna på kort och lång sikt hos plastkomponenter som används i fordonsbränslesystem.

I detta arbete har egenskaperna undersökts hos oförstärkt och glasfiberarmerad polyamid 12 (PA12), utsatt för tre olika bränslen (petroleumdiesel, biodiesel och en blandning av dessa (80/20)) vid hög temperatur. Interaktionen mellan polymeren och bränslet och tillhörande åldringsmekanismer hos polymeren (bränsleupptag, extraktion av monomer och oligomer, anlöpning och oxidation) befanns vara "generiska" i den mening att de inträffade, dock i olika grad, för alla bränslen. För glasfiberarmerad polyamid skedde åldrandet huvudsakligen i polyamid-matrisen och inte i gränsskiktet mellan matris och fiber. Semi-aromatisk polyamid visade bättre prestanda än alifatisk PA12 när dessa utsattes för bränslena.

På komponentnivå åldrades flerskikts-polyamid-baserade rör, med polyamid eller fluorpolymer som inre skikt, under ”fordons-lika förhållanden” med bränsle på insidan och luft på utsidan. Alla rör förstyvades under åldrandet men en försprödning inträffade endast för rören med polyamid som inre skikt. Jämfört med polyamiden uppvisade det inre skiktet av fluorpolymer betydligt bättre barriäregenskaper gentemot bränslet och inget material extraherades ut i bränslefasen. Mjukgöraravgången från ytterskikten av PA12 i kontakt med luft var diffusionsstyrd och följde ett linjärt Arrhenius-beteende i högtemperatur-området. Sambanden mellan mjukgöraravgång och förändringar i de mekaniska egenskaperna fastställdes.

Polyamiderna genomgick diffusionsbegränsad oxidation när de utsattes för luft och/eller bränsle, vilket resulterade i bildandet av ett tunt oxiderat ytskikt, vilket i sig bidrog till en avsevärd sänkning i brottöjning.

Brott-beteendet hos PA6 i luft vid hög temperatur studerades systematiskt, vilket ledde till att underliggande mekanismer som var ansvariga för minskningen av brottöjningen i tre distinkta stadier, kunde tas fram.

 

Ort, förlag, år, upplaga, sidor
KTH Royal Institute of Technology, 2019. s. 65
Serie
TRITA-CBH-FOU ; 2019:51
Nyckelord
Automotive, Ageing, Polyamide, Diesel, Biodiesel, Diffusion, Oxidation, Plasticizer migration, Mechanical properties, Fracture behavior., Fordon, Åldrande, Polyamid, Diesel, Biodiesel, Diffusion, Oxidation, Mjukgöraravgång, Mekaniska egenskaper, Brottegenskaper
Nationell ämneskategori
Polymerteknologi
Identifikatorer
urn:nbn:se:kth:diva-260472 (URN)978-91-7873-320-0 (ISBN)
Disputation
2019-10-25, F3, Lindstedtsvägen 26, Stockholm, 10:00 (Engelska)
Opponent
Handledare
Anmärkning

QC 2019-10-01

Tillgänglig från: 2019-10-01 Skapad: 2019-09-30 Senast uppdaterad: 2019-10-03Bibliografiskt granskad

Open Access i DiVA

Fulltext saknas i DiVA

Övriga länkar

Förlagets fulltextScopus

Personposter BETA

Wei, Xin-FengGedde, Ulf WHedenqvist, Mikael S.

Sök vidare i DiVA

Av författaren/redaktören
Wei, Xin-FengGedde, Ulf WHedenqvist, Mikael S.
Av organisationen
Fiber- och polymerteknologiPolymera material
I samma tidskrift
Polymer degradation and stability
Naturresursteknik

Sök vidare utanför DiVA

GoogleGoogle Scholar

doi
urn-nbn

Altmetricpoäng

doi
urn-nbn
Totalt: 152 träffar
RefereraExporteraLänk till posten
Permanent länk

Direktlänk
Referera
Referensformat
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annat format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annat språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf