Deterioration of automotive rubbers in liquid biofuels: A review
KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Polymera material. Scania CV AB, Sweden.ORCID-id: 0000-0002-7348-0004
KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Polymera material.
KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Polymera material.
Vise andre og tillknytning
2015 (engelsk)Inngår i: Renewable & sustainable energy reviews, ISSN 1364-0321, E-ISSN 1879-0690, Vol. 43, s. 1238-1248Artikkel, forskningsoversikt (Fagfellevurdert) Published
Abstract [en]

Concerns over the fast depletion of fossil fuels, environmental issues and stringent legislation associated with petroleum-based fuels have triggered a shift to bio-based fuels, as an alternative to meet the growing energy demand in the transportation sector. However, since conventional automobile fuel systems are adapted to petroleum-based fuels, switching to biofuels causes a severe deterioration in the performance of currently used rubber components. The degradation of the rubber materials in biofuels is complicated by the presence of different additives in biofuels and rubber compounds, by oxidation of biofuels and by the effects of thermomechanical loadings in the engine. This paper presents a comprehensive review of the effects of different types of biofuels, particularly biodiesel and bioethanol, on the physical, mechanical, morphological and thermal properties of elastomers under different exposure conditions. In addition, the literature data available on the variation of rubbers' resistance to biofuels with the changes in their monomer type and composition, cure system and additives content was also studied. The review essentially focuses on the compatibility of biofuels with acrylonitrile butadiene rubber, fluoroelastomers, polychloroprene rubber and silicon rubber, as the most commonly used automotive rubbers coming into contact with fuels during their service. The knowledge summarized in this study can help to develop a guideline on the selection of rubber for automotive parts designed to withstand biofuels.

sted, utgiver, år, opplag, sider
2015. Vol. 43, s. 1238-1248
Emneord [en]
Biofuels, Rubbers, Automobile fuel system, Degradation
HSV kategori
Identifikatorer
URN: urn:nbn:se:kth:diva-161100DOI: 10.1016/j.rser.2014.11.096ISI: 000348880600097Scopus ID: 2-s2.0-84919799253OAI: oai:DiVA.org:kth-161100DiVA, id: diva2:796176
Forskningsfinansiär
Swedish Energy Agency, 2011-006737
Merknad

QC 20150318

Tilgjengelig fra: 2015-03-18 Laget: 2015-03-09 Sist oppdatert: 2017-12-04bibliografisk kontrollert
Inngår i avhandling
1. Degradation of acrylonitrile butadiene rubber and fluoroelastomers in rapeseed biodiesel and hydrogenated vegetable oil
Åpne denne publikasjonen i ny fane eller vindu >>Degradation of acrylonitrile butadiene rubber and fluoroelastomers in rapeseed biodiesel and hydrogenated vegetable oil
2017 (engelsk)Doktoravhandling, med artikler (Annet vitenskapelig)
Abstract [en]

Biodiesel and hydrotreated vegetable oil (HVO) are currently viewed by the transportation sector as the most viable alternative fuels to replace petroleum-based fuels. The use of biodiesel has, however, been limited by the deteriorative effect of biodiesel on rubber parts in automobile fuel systems. This work therefore aimed at investigating the degradation of acrylonitrile butadiene rubber (NBR) and fluoroelastomers (FKM) on exposure to biodiesel and HVO at different temperatures and oxygen concentrations in an automated ageing equipment and a high-pressure autoclave. The oxidation of biodiesel at 80 °C was promoted by an increase in the oxygen partial pressure, resulting in the formation of larger amounts of hydroperoxides and acids in the fuel. The fatty acid methyl esters of the biodiesel oxidized less at 150 °C on autoclave aging, because the termination reactions between alkyl and alkylperoxyl radicals dominated over the initiation reactions. HVO consists of saturated hydrocarbons, and remained intact during the exposure. The NBR absorbed a large amount of biodiesel due to fuel-driven internal cavitation in the rubber, and the uptake increased with increasing oxygen partial pressure due to the increase in concentration of oxidation products of the biodiesel. The absence of a tan δ peak (dynamical mechanical measurements) of the bound rubber and the appearance of carbon black particles devoid of rubber suggested that the cavitation was caused by the detachment of bound rubber from particle surfaces. A significant decrease in the strain-at-break and in the Payne-effect amplitude of NBR exposed to biodiesel was explained as being due to the damage caused by biodiesel to the rubber-carbon-black network. During the high-temperature autoclave ageing, the NBR swelled less in biodiesel, and showed a small decrease in the strain-at-break due to the cleavage of rubber chains. The degradation of NBR in the absence of carbon black was due only to biodiesel-promoted oxidative crosslinking. The zinc cations released by the dissolution of zinc oxide particles in biodiesel promoted reduction reactions in the acrylonitrile part of the NBR. Heat-treated star-shaped ZnO particles dissolved more slowly in biodiesel than the commercial ZnO nanoparticles due to the elimination of inter-particle porosity by heat treatment. The fuel sorption was hindered in HVO-exposed NBR by the steric constraints of the bulky HVO molecules. The extensibility of NBR decreased only slightly after exposure to HVO, due to the migration of plasticizer from the rubber. The bisphenol-cured FKM co- and terpolymer swelled more than the peroxide-cured GFLT-type FKM in biodiesel due to the chain cleavage caused by the attack of biodiesel on the double bonds formed during the bisphenol curing. The FKM rubbers absorbed biodiesel faster, and to a greater extent, with increasing oxygen concentration. It is suggested that the extensive biodiesel uptake and the decrease in the strain-at-break and Young’s modulus of the FKM terpolymer was due to dehydrofluorination of the rubber by the coordination complexes of biodiesel and magnesium oxide and calcium hydroxide particles. An increase in the CH2-concentration of the extracted FKM rubbers suggested that biodiesel was grafted onto the FKM at the unsaturated sites resulting from dehydrofluorination.

sted, utgiver, år, opplag, sider
Stockholm, Sweden: KTH Royal Institute of Technology, 2017. s. 63
Serie
TRITA-CHE-Report, ISSN 1654-1081 ; 2017:9
Emneord
Degradation; Acrylonitrile butadiene rubber; Fluoroelastomers; Biodiesel; Hydrotreated vegetable oil; Cavitation; Bound rubber; Dehydrofluorination.
HSV kategori
Forskningsprogram
Fiber- och polymervetenskap
Identifikatorer
urn:nbn:se:kth:diva-202422 (URN)978-91-7729-274-6 (ISBN)
Disputas
2017-03-31, F3, 10:00 (engelsk)
Opponent
Veileder
Merknad

QC 20170227

Tilgjengelig fra: 2017-02-27 Laget: 2017-02-24 Sist oppdatert: 2017-06-26bibliografisk kontrollert

Open Access i DiVA

Fulltekst mangler i DiVA

Andre lenker

Forlagets fulltekstScopus

Personposter BETA

Akhlaghi, Shahin

Søk i DiVA

Av forfatter/redaktør
Akhlaghi, ShahinGedde, Ulf W.Hedenqvist, Mikael S.
Av organisasjonen
I samme tidsskrift
Renewable & sustainable energy reviews

Søk utenfor DiVA

GoogleGoogle Scholar

doi
urn-nbn

Altmetric

doi
urn-nbn
Totalt: 1080 treff
RefereraExporteraLink to record
Permanent link

Direct link
Referera
Referensformat
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf