Several Co-Cr alloys have been investigated by Differential Scanning Calorimetry (DSC) as well as by Differential Thermal Analysis (DTA) in the temperature range 298 - 1823 K. The compositional range investigated was from 0 to 87 wt.% Cr with special attention given to alloys with low Cr contents, i. e. 0 to 10 wt.% Cr. From the DSC measurements molar heat capacity values, phase transformation temperatures, enthalpies of transformation and Curie transition temperatures were derived. From the DTA measurements, the melting temperatures and melting enthalpies were evaluated. The trends obtained were compared with the results for pure Co as well as the proposed phase diagram reported in literature.