Effects of Nitride-Oxide Particles on Solidified Structure inFe-20mass%Cr Alloy Deoxidised with Ti/M (M = Zr or Ce)
KTH, School of Industrial Engineering and Management (ITM), Materials Science and Engineering, Applied Process Metallurgy.
KTH, School of Industrial Engineering and Management (ITM), Materials Science and Engineering, Applied Process Metallurgy.
KTH, School of Industrial Engineering and Management (ITM), Materials Science and Engineering, Applied Process Metallurgy.
KTH, School of Industrial Engineering and Management (ITM), Materials Science and Engineering, Applied Process Metallurgy.
Show others and affiliations
2010 (English)Report (Other academic)
Abstract [en]

The ratio of equiaxed grains on a cross section and average grain sizein Fe-20mass% Cr alloy deoxidised with Ti/M (M = Zr or Ce) were studiedas function of nitrogen content and particle characteristics such as sizedistribution, morphology and composition. Fe-20mass%Cr alloys weremelted at 1600ºC, deoxidised, cooled to 1400ºC followed by waterquenching. The particles were investigated on a surface of film filter afterelectrolytic extraction of metal samples with 10%AA electrolyte. It wasfound that the number of particles increases with increasing the N content.The as-cast solidification structure and grain size were clearly affected bythe number of oxide and oxide-nitride particles in Ti/Zr experiments. Theeffect in the Ti-Ce case was almost undetectable.

Place, publisher, year, edition, pages
Stockholm: KTH , 2010. , 40 p.
Series
KTH/MSE, 10:13
Keyword [en]
Fe-Cr alloy; Ti, Zr and Ce deoxidation, grain size distribution
National Category
Metallurgy and Metallic Materials
Identifiers
URN: urn:nbn:se:kth:diva-13327OAI: oai:DiVA.org:kth-13327DiVA: diva2:323684
Note
QC20100611Available from: 2010-06-11 Created: 2010-06-11 Last updated: 2010-06-11Bibliographically approved
In thesis
1. Inclusions and/or Particles Engineering for Grain Refining Purposes in Ferritic Fe-20mass%Cr alloys
Open this publication in new window or tab >>Inclusions and/or Particles Engineering for Grain Refining Purposes in Ferritic Fe-20mass%Cr alloys
2010 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

Compared to more common used austenitic stainless steels, ferritic stainless steels contain very low amounts of the expensive alloying element Ni. In addition, they have good corrosion properties, but are sometimes suffering from poor weldability and bad mechanical properties. This is mainly due to the presence of large grains after casting and large grain growth during heat treatment or welding. Processes for reducing the grain size (grain refining) of metal alloys are widely known and proven before to be suitable for many alloys. A successful grain refining process can increase the strength of an alloy without decreasing the ductility. This can be achieved by different methods, such as rolling or cooling. In this work, the focus has been on studying the aspect from a metallurgist point of view, to analyse the possibilities to create small particles in the liquid stage to enhance the solidification. The focus has been on oxide and nitride formation for nucleation of smaller grains during solidification.

This study was made by forming particles, develop the analysis methods and thereafter to study the effect of particles on the structure of a ferritic stainless steel. The particles were formed by additions of Ti, Ce and Zr in to a liquid Fe-20mass% Cr alloy containing different amounts of oxygen and nitrogen. The electrolytic extraction technique was used to achieve a good understanding of the reaction processes and the particles size, number, composition and morphology. The grain sizes and the particles were then studied in as-cast samples as well as in specimens heat treated for 60 minutes at 1200, 1300 and 1400°C in a Confocal Scanning Laser Microscope (CSLM). Also, based on Scanning Electron Microscope (SEM) determinations and Thermo-Calc calculations, the precipitated particles were divided as primary and secondary particles. Thereafter, the grain refining potential was studied for each of these types.

In this work, particles engineering by using small particles have been proven suitable for the Fe-20mass% Cr ferritic stainless steel alloys. Although the work has been based on small-scale samples and experiments, the results show good tendencies with respect to grain refining as well as a clear relationship between the particles in the steels and the microstructures. It was found that Ti-Ce additions in Fe-20mass% Cr alloys resulted in complex oxides including Ti, Ce and Cr. These oxides were observed to have high agglomeration tendencies and therefore to form larger particles or clusters. The grain refining potential on the solidification structure was insignificant, despite a relatively large amount of particles. However, Ti-Zr additions in Fe- 20mass% Cr alloys on the other hand resulted in primary precipitated particles such as ZrO2 and ZrO2+ZrN. Furthermore, ZrN nucleated ferrite during solidification, which lead to a clearly observed grain refining effect. This effect was also increased with an increased number of particles. The amount of particles (primary and secondary) was also found to increase with an increased amount of nitrogen. Secondary particles (mostly TiN) were precipitated near grain boundaries, which lead to a location based pinning effect of the grain growth during heat treatment at 1200 °C. This pinning effect was increased by an increased nitrogen content and thereby an increased number of particles. Finally, the pinning effect was clearly reduced during heat treatment at 1400 °C.

Place, publisher, year, edition, pages
Stockholm: KTH, 2010. x, 55 p.
Keyword
Inclusions, Particles, Grain size, High Cr, Ferritic, Grain refining, Solidification, Pinning effect, Stainless steel, Oxides, Nitrides
National Category
Metallurgy and Metallic Materials
Identifiers
urn:nbn:se:kth:diva-13012 (URN)978-91-7415-599-0 (ISBN)
Public defence
2010-05-20, F3, Lindstedtsvägen 26, KTH, Stockholm, 13:00 (English)
Opponent
Supervisors
Note
QC20100524Available from: 2010-05-24 Created: 2010-05-24 Last updated: 2011-09-19Bibliographically approved

Open Access in DiVA

fulltext(9775 kB)258 downloads
File information
File name FULLTEXT01.pdfFile size 9775 kBChecksum SHA-512
097da7a4df96a10bf2bf7c5c363011666d39094342b8b2d58f0e8b9645e05f3df2949ca34e56e8083ca9ca6ba7fdedd3e65aa7397695614c01f598203cc60326
Type fulltextMimetype application/pdf

Search in DiVA

By author/editor
Janis, JesperNakajima, KeijiKarasev, AndreyJonsson, StefanJönsson, Pär
By organisation
Applied Process Metallurgy
Metallurgy and Metallic Materials

Search outside of DiVA

GoogleGoogle Scholar
Total: 258 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

urn-nbn

Altmetric score

urn-nbn
Total: 181 hits
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf