2004 (English)In: Acta Materialia, ISSN 1359-6454, E-ISSN 1873-2453, Vol. 52, no 7, 1847-1858 p.Article in journal (Refereed) Published
The deformation during sintering under an applied uniaxial load was investigated experimentally for two WC-Co cemented carbides with different grain size. The lower applied loads changed only the relative magnitude of axial and radial shrinkages, whereas the higher loads also affected the volumetric strain. Local maxima in shrinkage rate were found at relative densities close to 0.8 for all sintering conditions. The constitutive parameters uniaxial viscosity, Poisson's ratio and sintering stress were empirically modelled as functions of temperature and relative density.
Place, publisher, year, edition, pages
2004. Vol. 52, no 7, 1847-1858 p.
sintering, cermets, high temperature deformation, constitutive equations, modelling, cemented carbides, hardmetals, viscosity, compacts, system, models
Metallurgy and Metallic Materials
IdentifiersURN: urn:nbn:se:kth:diva-23356DOI: 10.1016/j.actamat.2003.12.024ISI: 000221001300009ScopusID: 2-s2.0-1842607232OAI: oai:DiVA.org:kth-23356DiVA: diva2:342054
QC 20100525 201110282010-08-102010-08-102011-10-28Bibliographically approved