The effect of polymer modification on hot mix asphalt fracture at tensile loading conditions
2010 (English)In: The international journal of pavement engineering, ISSN 1029-8436, Vol. 11, no 5, 403-413 p.Article in journal (Refereed) Published
A laboratory investigation was conducted to evaluate the effect of both cross-linked and linear styrene-butadiene-styrene (SBS) modifiers on the cracking resistance of hot mix asphalt (HMA) mixtures. Five types of asphalt mixtures composed by the same aggregate gradation but different asphalt binders were produced in the laboratory. The cracking performances of the mixtures were evaluated using a viscoelastic fracture mechanics-based model entitled 'HMA Fracture Mechanics'. Crack localisation and crack growth were investigated performing the indirect tensile test and the semi-circular bending test. A digital image correlation system capable of providing full-field strain maps was applied. The results show the benefit of SBS modifiers to the mixture's cracking resistance in terms of reduced rate of damage accumulation and increased tensile limits to failure. Finally, significant damage and first fracture have shown to be strongly more localised in modified specimens than in the unmodified one.
Place, publisher, year, edition, pages
2010. Vol. 11, no 5, 403-413 p.
hot mix asphalt, semi-circular bending test, Superpave indirect tension test, styrene-butadiene-styrene modifier, digital image correlation
IdentifiersURN: urn:nbn:se:kth:diva-29425DOI: 10.1080/10298436.2010.488735ISI: 000280620500008ScopusID: 2-s2.0-77955359178OAI: oai:DiVA.org:kth-29425DiVA: diva2:397629
QC 201102152011-02-152011-02-022011-02-15Bibliographically approved