Influence of slag properties on the amount of solid precipitates in high-chromium EAF steelmaking
KTH, School of Industrial Engineering and Management (ITM), Materials Science and Engineering, Applied Process Metallurgy.
KTH, School of Industrial Engineering and Management (ITM), Materials Science and Engineering, Applied Process Metallurgy.
2011 (English)In: Steel Grips - Journal of Steel and Related Materials, ISSN 1611-4442, Vol. 9, 355-359 p.Article in journal (Other academic) Published
Abstract [en]

The total amount of solid particles as a parameter influencing the viscosity and the foaming properties of the slag was investi-gated. In this context, the amount of these particles for different process conditions was quantified. In addition, the effect of the process conditions on the total amount of the particles was studied. More specifically, some parameter studies were carried out in order to determine the influence of chromium oxide (Cr2O3) content, calcium oxide (CaO) content, basicity and temperature on the total amount of solid particles. The interactions between the process conditions were also taken into account. The results were visualized in diagrams and thereafter discussed in detail.

Place, publisher, year, edition, pages
2011. Vol. 9, 355-359 p.
Keyword [en]
EAF, slag, amount of solid precipitates, viscosity, foamability, computational thermodynamics, high-chromium stainless steel, basicity
URN: urn:nbn:se:kth:diva-33772OAI: diva2:417447
QC 20120328. Updated from submitted to published.Available from: 2011-05-17 Created: 2011-05-17 Last updated: 2012-03-28Bibliographically approved
In thesis
1. A Study of EAF High-Chromium Stainless Steelmaking Slags Characteristics and Foamability
Open this publication in new window or tab >>A Study of EAF High-Chromium Stainless Steelmaking Slags Characteristics and Foamability
2011 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

A good slag practice is essential for production of a high-quality stainless steel. In addition, the electrical and material efficiency of the electric arc furnace (EAF) can considerably be improved by a good slag practice. The metallurgical properties of the slag are strongly influenced by its high-temperature microstructure. Thus, characterization of the phases within the EAF slag as well as the determination of the amount of these phases is of high importance.In addition, the knowledge about the chemical composition of the liquid slag and solid phases at the process temperatures is instrumental in developing a good slag practice.In order to study the slag in EAF high-chromium stainless steelmaking, slag samples were collected from 14 heats of AISI 304L steel (two samples per heat) and 7 heats of duplex steel (three samples per heat).The selected slag samples were petrographically studied both using scanning electron microscopy equipped with energy dispersive X-ray spectroscopy (SEM-EDS) and light optical microscopy (LOM). In some cases, X-ray diffraction (XRD) analyses were also performed. Moreover, computational thermodynamics was used to determine the equilibrium phases in the EAF steelmaking slags at the process temperatures. In addition, parameter studies were performed on the factors influencing the equilibria.More specifically, a petrographical and thermodynamic characterization was performed on the EAF austenitic steelmaking slags. Thereafter, the microstructural evolution of the slag during the EAF duplex steelmaking process was investigated. Moreover, an investigation with focus on the total amount of precipitates within the high-chromium stainless steelmaking slags was done. Finally, the foamability of these slags was quantified and evaluated.The petrographic investigations showed that, during the refining stage, in both austenitic and duplex cases, the main constituent of the EAF slag is a melt consisting of liquid oxides. In addition, the slag samples contain solid spinel particles. However, before ferrosilicon-addition (FeSi), the slag may also contain solid stoichiometric calcium chromite. Moreover, depending on the slag basicity, the slag may contain solid dicalcium silicate at the process temperatures.The evolution of the slag during the refining stage of the EAF was graphically illustrated in the calculated isothermal phase diagrams for the slag system Al2O3-Cr2O3-CaO-MgO-SiO2-TiO2.It was found that the only critical parameter affecting the amount of solid spinel particles in the slag is the chromium-oxide content. More specifically, it was shown that the amount of the spinel particles in the slag increases with an increased chromium-oxide content of the slag. It wasvialso shown that a higher basicity and a lower temperature of the slag contribute to the dicalcium silicate precipitation.In order to evaluate and quantify the foamability of the slags, the slag’s physical properties influencing its foaming index were determined. Computational thermodynamics was used as a tool to calculate the weight fractions of the solid phases within the slag at different EAF process stages. The computational thermophysics was used to estimate the viscosity of the liquid part of the slag samples at the process temperatures. The apparent viscosity of the samples was calculated by combining the above results. By estimating the density, surface tension and the foaming-gas bubble size, the foaming index of the slag samples were quantified. It could be shown that the foaming index of the EAF high-chromium stainless steelmaking slag may be on its minimum as the slag’s basicity takes a value in the range of 1.2 – 1.5. A basicity value of around 1.50 – 1.60 can be suitable for enhancing the foaming index of the slag, during the refining period in EAF high-chromium stainless steelmaking.

Place, publisher, year, edition, pages
Stockholm: KTH Royal Institute of Technology, 2011. xii, 66 p.
High-chromium stainless steel, EAF, Slag, Microstructural characterization, Microstructural Evolution, Computational thermodynamics, Solid particles, Viscosity, Foamability, Basicity
National Category
Metallurgy and Metallic Materials
urn:nbn:se:kth:diva-33754 (URN)978-91-7415-968-4 (ISBN)
Public defence
2011-05-24, Sal F3, Lindstedtvägen 26, KTH, Stockholm, 10:00 (English)
Available from: 2011-05-17 Created: 2011-05-16 Last updated: 2011-05-17Bibliographically approved

Open Access in DiVA

No full text

Search in DiVA

By author/editor
Mostafaee, SamanJönsson, Pär
By organisation
Applied Process Metallurgy
In the same journal
Steel Grips - Journal of Steel and Related Materials

Search outside of DiVA

GoogleGoogle Scholar
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 77 hits
ReferencesLink to record
Permanent link

Direct link