Thermal diffusivity of TiAlNb and AN alloys - the European IMPRESS project
KTH, School of Industrial Engineering and Management (ITM), Materials Science and Engineering, Materials Process Science.
Show others and affiliations
2008 (English)In: Diffusion In Solids And Liquids III / [ed] Ochsner, A; Murch, GE, 2008, Vol. 273-276, 375-380 p.Conference paper (Refereed)
Abstract [en]

The thermal diffusivities of some industrially important alloys have been measured as a part of the EU funded Intermetallic Materials Processing in Relation to Earth and Space Solidification (IMPRESS) project which is coordinated by the European Space Agency (ESA). The thermal diffusivities of the alloys were measured by the Laser flash method with a carefully designed gas cleaning system to remove traces of oxygen from the argon atmosphere. In the present work, the thermal diffusivity of TiAlNb (Ti46.1A145.9Nb8 at %) and AlNi alloy (Al-Ni31.5 at %) alloys have been measured independently at Royal Institute of Technology, Sweden (KTH) and National Physical Laboratory, UK (NPL). The results from both laboratories were consistent, and have been compared with predictions of phase transformation temperatures calculated using Thermo Calc and MTDATA software. Generally the variation of thermal diffusivity appears to be related to the phase transformation. However, one anomaly observed in the present work on TiAlNb was a maximum thermal diffusivity value at about HOOK. No corresponding peak was found for the density, p, the specific heat capacity, C, or the electrical resistivity, 1/sigma, which were also measured as part of the project. In view of the fact that the thermal diffusivity could be related to electrical conductivity by the Wiedemann-Franz law describing electronic contribution to heat conduction, the present results indicate a non-electron contribution. This aspect is being currently investigated further. The recommended thermal diffusivity value of TiAlNb and AIM alloys were obtained as follows. TiAlNb alloy: alpha = 3.75+ 5.16.10(-3)T+1.89.10(-6) T-2-2.69.10(-9) T-3 [10(-6) m(2) s(-1)] (293 K < T < 1573 K) AlNi alloy: alpha = 4.77+ 5.41.10(-2)T - 7.14.10(-5)T(2)+ 2.88.10(-8)T(3) [10(-6) m(2)/s] (373K < T < 943K).

Place, publisher, year, edition, pages
2008. Vol. 273-276, 375-380 p.
, Defect And Diffusion Forum, ISSN 1012-0386 ; 273-276
Keyword [en]
thermal diffusivity, thermal conductivity, TiAlNb alloy, AIM alloy, Wiedemann-Franz law
National Category
Metallurgy and Metallic Materials
URN: urn:nbn:se:kth:diva-38433DOI: 10.4028/ 000254387700063OAI: diva2:436851
3rd International Conference on Diffusion in Solids and Liquids Location: Algarve, PORTUGAL Date: JUL 04-06, 2007
Available from: 2011-08-25 Created: 2011-08-25 Last updated: 2011-08-25Bibliographically approved

Open Access in DiVA

No full text

Other links

Publisher's full text

Search in DiVA

By author/editor
Matsushita, TaishiSeetharaman, Seshadri
By organisation
Materials Process Science
Metallurgy and Metallic Materials

Search outside of DiVA

GoogleGoogle Scholar
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Altmetric score

Total: 22 hits
ReferencesLink to record
Permanent link

Direct link