Mechanical ana corrosion properities of P/M-HIP super duplex stainless steel after different industrial heat treatments as used for large components
2004 (English)In: Materials Science and Technology, ISSN 0267-0836, E-ISSN 1743-2847, Vol. 20, no 5, 641-644 p.Article in journal (Refereed) Published
Mechanical tensile and impact toughness tests and critical pitting corrosion temperature (CPT) tests were performed on samples of Duplok 27, a P/M-HIP duplex stainless steel containing copper, after heat treatments simulating industrial heat treatments of large components. It was shown that copper alloying has positive effects on mechanical tensile properties leading to hardening and more uniform deformation. No negative effects of copper alloying on corrosion resistance properties were found. A drastic drop in impact toughness values and CPT of samples cooled at controlled cooling rates is explained by the precipitation of intermetallic secondary phases or their precursors. Lower CPT of a NG-GTAW (narrow gap gas tungsten arc welding) welded joint is explained by the lower level of alloying than that of the base material. The high temperature region of precipitation of intermetallic secondary phases is shifted towards higher temperatures than assumed for Duplok 27 P/M-HIP duplex stainless steel.
Place, publisher, year, edition, pages
2004. Vol. 20, no 5, 641-644 p.
PM duplex stainless steel, corrosion properties, mechanical properties, heat treatment
IdentifiersURN: urn:nbn:se:kth:diva-44950DOI: 10.1179/026708304225011946ISI: 000222076300013ScopusID: 2-s2.0-2942557042OAI: oai:DiVA.org:kth-44950DiVA: diva2:453242
QC 201111012011-11-012011-10-262011-11-01Bibliographically approved