Fabrication, spark plasma consolidation, and thermoelectric evaluation of nanostructured CoSb3
KTH, School of Industrial Engineering and Management (ITM), Materials Science and Engineering.
KTH, School of Information and Communication Technology (ICT), Materials- and Nano Physics, Functional Materials, FNM.ORCID iD: 0000-0001-5380-975X
Show others and affiliations
2014 (English)In: Journal of Alloys and Compounds, ISSN 0925-8388, Vol. 612, 293-300 p.Article in journal (Refereed) Published
Abstract [en]

Nanostructured powders of thermoelectric (TE) CoSb3 compounds were synthesized using a chemical alloying method. This method involved co-precipitation of oxalate precursors in aqueous solution with controlled pH, followed by thermochemical treatments including calcination and reduction to produce stoichiometric nanostructured CoSb3. Moreover, CoSb3 nanoparticles were consolidated by spark plasma sintering (SPS) with a very brief processing time. Very high compaction densities (>95%) were achieved and the grain growth was almost negligible during consolidation. An iterative procedure was developed to maintain pre-consolidation particle size and to compensate Sb evaporation during reduction. Significant changes in particle size and morphology were observed, and the post-reduction cooling was found to be an important stage in the process. The spark plasma sintering (SPS) parameters were optimized to minimize the grain growth while achieving sufficient densification. Grain sizes in the range of 500 nm to 1 mu m, with compaction density of 95-98% were obtained. Preliminary measurements of thermal diffusivity and conductivity showed the dependence on grain size as well as on porosity. TE transport properties were measured in the temperature range of 300-650 K. Sample showed p-type behavior with a positive Seebeck coefficient, which increases with increasing temperature. Electrical conductivity measurements indicate metallic behavior and it decreases with increasing temperature. Thermal conductivity also decreases with increasing temperature and major contribution is due to the lattice component. A TE figure of merit of 0.15 was achieved for high purity CoSb3 nanostructured TE material at 650 K and these results are comparable with the values reported for the best unfilled/undoped CoSb3 in the literature.

Place, publisher, year, edition, pages
2014. Vol. 612, 293-300 p.
Keyword [en]
Nanostructured, CoSb3 skutterudites TE, Spark plasma sintering
National Category
Chemical Sciences
URN: urn:nbn:se:kth:diva-149957DOI: 10.1016/j.jallcom.2014.05.119ISI: 000339692300047ScopusID: 2-s2.0-84903209835OAI: diva2:745080
EU, FP7, Seventh Framework Programme, EM11-0002Swedish Foundation for Strategic Research , EM11-0002

QC 20140909

Available from: 2014-09-09 Created: 2014-08-29 Last updated: 2014-09-09Bibliographically approved

Open Access in DiVA

No full text

Other links

Publisher's full textScopus

Search in DiVA

By author/editor
Khan, AbdullahSaleemi, MohsinMuhammed, MamounToprak, Muhammet S.
By organisation
Materials Science and EngineeringFunctional Materials, FNM
In the same journal
Journal of Alloys and Compounds
Chemical Sciences

Search outside of DiVA

GoogleGoogle Scholar
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Altmetric score

Total: 32 hits
ReferencesLink to record
Permanent link

Direct link