Disaggregation and Anionic Activation of Nanodiamonds Mediated by Sodium Hydride: A New Route to Functional Aliphatic Polyester-Based Nanodiamond Materials
KTH, School of Chemical Science and Engineering (CHE), Fibre and Polymer Technology, Polymer Technology.
KTH, School of Chemical Science and Engineering (CHE), Fibre and Polymer Technology, Polymer Technology.
Show others and affiliations
2014 (English)In: Particle & particle systems characterization, ISSN 0934-0866, E-ISSN 1521-4117, Vol. 32, no 1, 35-42 p.Article in journal (Refereed) Published
Abstract [en]

Polylactide-modified nanodiamond particles (n-DP-g-PLA) are prepared by sodium-hydride-activated nanodiamond-initated anionic ring-opening polymerization. Activated nanodiamond particles repel each other, preventing agglomeration during the polymerization. This universal modification provides a platform for the functionalization of all types of nanoparticles containing hydroxyl groups.

Place, publisher, year, edition, pages
2014. Vol. 32, no 1, 35-42 p.
Keyword [en]
Amphiphilic graft, Core-shell composite, Grafting from, Lactide, Nanoparticle
National Category
Other Chemistry Topics
URN: urn:nbn:se:kth:diva-152607DOI: 10.1002/ppsc.201400098ISI: 000347727600004ScopusID: 2-s2.0-84920918909OAI: diva2:750621

QC 20150227

Available from: 2014-09-29 Created: 2014-09-29 Last updated: 2015-02-27Bibliographically approved
In thesis
1. Engineering and Functionalization of Degradable Scaffolds for Medical Implant Applications
Open this publication in new window or tab >>Engineering and Functionalization of Degradable Scaffolds for Medical Implant Applications
2014 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

The treatment of bone defects is facing the situation of lacking donations for autotransplantation. As a valid approach, scaffold-based tissue engineering combines the construction of well-defined porous scaffolds with advanced cell culturing technology to guide tissue regeneration. The role for the scaffold is to provide a suitable environment with a sufficient mechanical stiffness, supports for cell attachment, migration, nutrients and metabolite transport and space for cell remodeling and tissue regeneration. The random copolymers poly(L-lactide-co-ɛ-caprolactone) (poly(LLA-co-CL)) and poly(L-lactide-co-1,5-dioxepan-2-one) (poly(LLA-co-DXO)) have been successfully incorporated into 3D porous scaffolds to induce specific interactions with cells and direct osteogenic cell differentiation. In this thesis, these scaffolds have been modified in chemical and physical ways to map and understand requirements for bone regeneration. Scaffold functionalities and properties, such as hydrophilicity, stiffness, size/shape, and reproducibility, were studied. The hydrophilicity was varied by adding 3–20 % (w/w) Tween 80 to poly(LLA-co-CL) and poly(LLA-co-DXO) respectively, which resulted in contact angles from 35° to 15°. With 3 % Tween 80, the resultant mechanical and thermal properties were similar to pristine polymer materials. Tween 80 did not significantly influence cell attachment or proliferation but did stimulate the mRNA expression of osteogenetic markers. The surface functionality and mechanical properties were altered by introducing nanodiamond particles (n-DP) into poly(LLA-co-CL) scaffolds by means of surface physisorption or hybrid blending. Scaffold with n-DP physisorbed showed improved cell attachment, differentiation, and bone reformation. Hybrid n-DP/poly(LLA-co-CL) composites were obtained by direct blending of polylactide modified n-DP (n-DP-PLA) with poly(LLA-coCL). The n-DP-PLA was prepared by sodium hydride-mediated anionic polymerization using n-DP as the initiator. Prepared n-DP-PLA could be dispersed homogenously in organic solvents and blended with poly(LLA-coCL) solution. The n-DP-PLA particles were homogenously distributed in the composite material, which significantly improved mechanical properties. For comparison, the addition of benzoquinone-modified n-DP (n-DP-BQ) did not reinforce poly(LLA-co-CL). This indicated the importance of specific surface grafting, which determined different particle-polymer interactions. For the treatment of critical size defects, a large porous poly(LLA-co-CL) scaffold (12.5 mm diameter × 25 mm thickness) was developed and produced by molding and salt-leaching methods. The large porous scaffolds were evaluated in a scaffold-customized perfusion-based bioreactor system. It was obvious that the scaffold could support improved cell distribution and support the stimulation of human mesenchymal stem cell (hMSC) especially with dynamic flow in a bioreactor. To improve the scaffolding technique, a three-dimensional fiber deposition (3DF) technique was employed to build layer-based scaffolds. Poly(LLA-coCL) scaffolds produced by the 3DF method showed enhanced mechanical properties and a homogeneous distribution of human osteoblasts (hOBs) in the scaffolds. Although poly(LLA-co-CL) was thermally degraded, the degradation did not influence the scaffold mechanical properties. Based on the computerized design, a 3DF scaffold of amorphous copolymer poly(LLAco-CL) provides high-precision control and reproducibility. In summary, the design of porous scaffolds is one of the essential factors in tissue engineering as to mimicking the intrinsic extracellular environment. For bone tissue engineering, an optimized scaffold can maintain a contact angle greater than 35 degrees. Pristine or modified n-DP, introduced as an additive by surface physisorption or direct blending, can improve scaffold mechanical properties and cell response. Various sizes of scaffolds can be easily produced by a mold-mediated salt-leaching method. However, when 100 % reproducibility is required, the 3DF method can be used to create customizable scaffolds.

Place, publisher, year, edition, pages
Stockholm: KTH Royal Institute of Technology, 2014. 73 p.
TRITA-CHE-Report, ISSN 1654-1081 ; 2014:36
Tissue engineering, nanodiamond, scaffold, bioreactor
National Category
Polymer Technologies
Research subject
Fibre and Polymer Science
urn:nbn:se:kth:diva-152605 (URN)978-91-7595-256-7 (ISBN)
Public defence
2014-10-17, Kollegiesalen, Brinellvägen 8, KTH, Stockholm, 13:44 (English)
EU, FP7, Seventh Framework Programme, Vascubone

QC 20140929

Available from: 2014-09-29 Created: 2014-09-29 Last updated: 2014-09-29Bibliographically approved

Open Access in DiVA

No full text

Other links

Publisher's full textScopus

Search in DiVA

By author/editor
Sun, YangOlsén, PeterAlbertsson, Ann-ChrisineFinne-Wistrand, Anna
By organisation
Polymer Technology
In the same journal
Particle & particle systems characterization
Other Chemistry Topics

Search outside of DiVA

GoogleGoogle Scholar
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Altmetric score

Total: 158 hits
ReferencesLink to record
Permanent link

Direct link