Non-woven textilier från träfibrer genom papperstillverkningsmetoder
KTH, School of Chemical Science and Engineering (CHE).
2015 (Swedish)Independent thesis Advanced level (degree of Master (Two Years)), 20 credits / 30 HE creditsStudent thesisAlternative title
Investigation of making nonwoven textiles with wood fibres and papermaking technique (English)
Abstract [sv]

Idag är den största delen av textilierna antingen olje-(60 %) eller bomullsbaserade (30 %). Det är enbart en liten del som är baserade på träfibrer. Ett ökande behov av förnyelsebara textilier föreligger. Samtidigt är ett minskade pappersbehov en drivkraft till att använda de existerande pappersmaskinerna till att tillverka icke vävda textilliknande material. Till skillnad från vävda material kan materialet tillverkas direkt istället för att först tillverka trådar från fibrer. Möjligheter att ta fram textillika material av cellulosafibrer undersöktes. Dynamiska ark gjorda av en blandning av barrmassa och en blandning av barr- och lövmassa med 0, 55 och 70 vikt% polymjölksyra, PLA, tillverkades. Arken pressades ihop två och två med ett mellanlager av Expancel mikrosfärer och bindemedel. Mowilith DM 105 och Primal LT-2949 Emulsion

användes som bindemedel. En jämförelse gjordes med ark med enbart bindemedel som mellanlager.

 

En subjektiv utvärdering av vilket förhållande mellan Expancel mikrosfärer och bindemedel som var bäst lämpad gjordes. För utvärderingen ytbehandlades ett standard papper med 70 vikt% PLA. Den sats med högst koncentration av Expancel mikrosfärer som band bra till bindemedelet valdes. Draghållfastheten testades genom dragprovning enligt ISO 1924-2:1994 men med endast

5 prover istället för 10.  Dragprovningen visade att tillsatsen av Expancel mikrosfärer ökade töjningen hos materialet. Materialen med högst koncentration av PLA gav den mjukaste känslan men också lägst styrka.

Abstract [en]

Today the main parts of textiles are either oil (60 %) or cotton based (30 %). It is only a small portion which is based on wood fibres. An increasing demand of renewable textiles is forthcoming. At the same time a decreasing demand of paper is one of the motivation of using

the existing paper machines to produce nonwoven textile-like materials. Unlike woven fabrics the fabric can be manufactured directly rather than first producing yarn from fibres. Possibilities of developing a textile-like material of cellulose fibres were investigated. Dynamic lab sheets made of a mix of softwood pulp and a mix of softwood and birch pulp with 0, 55 and 70 weight % Poly(lactic acid), PLA, were manufactured. The sheets was pressed together two and two with a middle layer of Expancel microspheres and binder. Mowilith DM 105 and Primal LT-2949 emulsion were used as binders. A comparison was made between sheets with only binder as the middle layer.

 

A subjective evaluation of which ratio between Expancel microspheres and binder material was best suited was made. For the evaluation a paper containing 70 weight% PLA was coated. The batch with highest concentration of Expancel microspheres, which bonded well to the binder, was chosen. The tensile strength was measured according to ISO 1924-2:1994 but with only 5 test samples instead of 10. The tensile tests showed that with Expancel microspheres resulted in increase of elongation of the material. The materials with the highest concentration of PLA had softest feeling but also lowest strength.

 

Place, publisher, year, edition, pages
2015. , 56 p.
Keyword [en]
Textile-like materials, nonwoven, cellulose, wood fibres, Expancel microspheres
National Category
Textile, Rubber and Polymeric Materials
Identifiers
URN: urn:nbn:se:kth:diva-173657OAI: oai:DiVA.org:kth-173657DiVA: diva2:854315
Available from: 2015-09-16 Created: 2015-09-16 Last updated: 2015-09-16Bibliographically approved

Open Access in DiVA

fulltext(1413 kB)210 downloads
File information
File name FULLTEXT01.pdfFile size 1413 kBChecksum SHA-512
a2d43ad90e291afa97efc59102d63d98002fc7ae186df91209388cf0e2a60f46639a9d304b6dfc38a0a3336114a5124bbba9689666002ec773ee4b7846cd7a38
Type fulltextMimetype application/pdf

By organisation
School of Chemical Science and Engineering (CHE)
Textile, Rubber and Polymeric Materials

Search outside of DiVA

GoogleGoogle Scholar
Total: 210 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

urn-nbn

Altmetric score

urn-nbn
Total: 127 hits
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf