Endre søk
Begrens søket
1 - 13 of 13
RefereraExporteraLink til resultatlisten
Permanent link
Referera
Referensformat
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf
Treff pr side
  • 5
  • 10
  • 20
  • 50
  • 100
  • 250
Sortering
  • Standard (Relevans)
  • Forfatter A-Ø
  • Forfatter Ø-A
  • Tittel A-Ø
  • Tittel Ø-A
  • Type publikasjon A-Ø
  • Type publikasjon Ø-A
  • Eldste først
  • Nyeste først
  • Skapad (Eldste først)
  • Skapad (Nyeste først)
  • Senast uppdaterad (Eldste først)
  • Senast uppdaterad (Nyeste først)
  • Disputationsdatum (tidligste først)
  • Disputationsdatum (siste først)
  • Standard (Relevans)
  • Forfatter A-Ø
  • Forfatter Ø-A
  • Tittel A-Ø
  • Tittel Ø-A
  • Type publikasjon A-Ø
  • Type publikasjon Ø-A
  • Eldste først
  • Nyeste først
  • Skapad (Eldste først)
  • Skapad (Nyeste først)
  • Senast uppdaterad (Eldste først)
  • Senast uppdaterad (Nyeste først)
  • Disputationsdatum (tidligste først)
  • Disputationsdatum (siste først)
Merk
Maxantalet träffar du kan exportera från sökgränssnittet är 250. Vid större uttag använd dig av utsökningar.
  • 1.
    Kaldéus, Tahani
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Centra, Wallenberg Wood Science Center. KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Surface modification approaches of cellulose nanofibrils and their effect on dispersibility2019Doktoravhandling, med artikler (Annet vitenskapelig)
    Abstract [en]

    In the strive to find and develop sustainable bio-based materials an increased interest for nanocellulosic materials as attractive alternatives has arisen during the past decades. This can be attributed to their abundant renewability, remarkable inherent mechanical properties and their capability to be chemically modified. Cellulose nanofibrils (CNFs) are commonly obtained from wood pulp fibres and prepared through mechanical, chemical and/or enzymatic treatments. However, due to their hydrophilic nature and tendency to self-aggregate, their surface chemistry need to be altered to fully utilise their inherent properties and enable their usage in conventional large-scale industrial processes.

    This thesis work focuses on elucidating the fundamental aspects of the colloidal stability of highly concentrated CNF dispersions and the redispersibility of dried CNFs. Small amounts of amine-terminated poly(ethylene glycol) (PEG) were used to sterically stabilise the CNFs at higher fibril concentrations and delay the dispersion-arrested state transition (Paper I). The redispersibility of dried CNFs was studied for differently charged CNFs as a function of redispersing agents such as carboxymethyl cellulose (CMC), PEG and lignin (Paper II).

    This thesis presents green, facile modification approaches as well as strategies for improved dispersibility and compatibility with polymer matrices. The commercially established carboxymethylation process was expanded with a subsequent functionality step, yielding a mild, versatile one-pot protocol for the preparation of bi-functional CNFs (Paper III). Further, reactive amphiphilic macromolecules with targeted side-chain functionalities were used to compatibilise the CNF surface by water-based approaches. In the first study, a macroinitiator was used for the development of a versatile, yet facile, protocol for the controlled polymerisation of both hydrophilic and hydrophobic monomers in water from the CNF surface (Paper IV). In the second study, a reactive macro-compatibiliser was used to molecularly engineer the interface between CNFs and a polymer matrix by reactive-melt processing, yielding nanocomposites with improved stiffness while maintaining the deformability (Paper V).

    Fulltekst tilgjengelig fra 2020-02-22 11:00
  • 2.
    Kaldéus, Tahani
    et al.
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi. KTH, Skolan för kemivetenskap (CHE), Centra, Wallenberg Wood Science Center.
    Carlmark, Anna
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi.
    Malmström, Eva
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi.
    Controlling colloidal stability in nanofibrillar systems by surface modification2016Inngår i: Abstracts of Papers of the American Chemical Society, ISSN 0065-7727, Vol. 251Artikkel i tidsskrift (Annet vitenskapelig)
  • 3.
    Kaldéus, Tahani
    et al.
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Centra, Wallenberg Wood Science Center.
    Larsson, Per Tomas
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Centra, Wallenberg Wood Science Center. RISE Bioecon, Drottning Kristinas Väg 61, S-11486 Stockholm, Sweden..
    Boujemaoui, Assya
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    Malmström, Eva
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    One-pot preparation of bi-functional cellulose nanofibrils2018Inngår i: Cellulose (London), ISSN 0969-0239, E-ISSN 1572-882X, Vol. 25, nr 12, s. 7031-7042Artikkel i tidsskrift (Fagfellevurdert)
    Abstract [en]

    Herein, we present a route to obtain bi-functional cellulose nanofibrils (CNF) by a one-pot approach using an already established functionalisation route, carboxymethylation, to which a subsequent functionalisation step, allylation or alkynation, has been added in the same reaction pot, eliminating the need of solvent exchange procedures. The total charge of the fibres and the total surface charge of the nanofibrils were determined by conductometric and polyelectrolyte titration, respectively. Furthermore, the allyl and alkyne functionalised cellulose were reacted with methyl 3-mercaptopropionate and azide-functionalised disperse red, respectively, to estimate the degree of functionalisation. The samples were further assessed by XPS and FT-IR. Physical characteristics were evaluated by CP/MAS C-13-NMR, XRD, AFM and DLS. This new approach of obtaining bi-functionalised CNF allows for a facile and rapid functionalisation of CNF where chemical handles can easily be attached and used for further modification of the fibrils.

  • 4.
    Kaldéus, Tahani
    et al.
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Centra, Wallenberg Wood Science Center.
    Leggieri, Maria Rosella Telaretti
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    Sanchez, Carmen
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    Malmström, Eva
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    All-Aqueous SI-ARGET ATRP from Cellulose Nanofibrils Using Hydrophilic and Hydrophobic Monomers2019Inngår i: Biomacromolecules, ISSN 1525-7797, E-ISSN 1526-4602, Vol. 20, nr 5, s. 1937-1943Artikkel i tidsskrift (Fagfellevurdert)
    Abstract [en]

    An all-water-based procedure for "controlled" polymer grafting from cellulose nanofibrils is reported. Polymers and copolymers of poly(ethylene glycol) methyl ether methacrylate (POEGMA) and poly(methyl methacrylate) (PMMA) were synthesized by surface-initiated activators regenerated by electron transfer atom transfer radical polymerization (SI-ARGET ATRP) from the cellulose nanofibril (CNF) surface in water. A macroinitiator was electrostatically immobilized to the CNF surface, and its amphiphilic nature enabled polymerizations of both hydrophobic and hydrophilic monomers in water. The electrostatic interactions between the macroinitiator and the CNF surface were studied by quartz crystal microbalance with dissipation energy (QCM-D) and showed the formation of a rigid adsorbed layer, which did not desorb upon washing, corroborating the anticipated electrostatic interactions. Polymerizations were conducted from dispersed modified CNFs as well as from preformed modified CNF aerogels soaked in water. The polymerizations yielded matrix-free composite materials with a CNF content of approximately 1-2 and 3-6 wt % for dispersion-initiated and aerogel-initiated CNFs, respectively.

  • 5.
    Kaldéus, Tahani
    et al.
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Ytbehandlingsteknik. KTH, Skolan för kemivetenskap (CHE), Centra, Wallenberg Wood Science Center.
    Nordenström, Malin
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi. KTH, Skolan för kemivetenskap (CHE), Centra, Wallenberg Wood Science Center.
    Carlmark, Anna
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Wågberg, Lars
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi. KTH, Skolan för kemivetenskap (CHE), Centra, Wallenberg Wood Science Center.
    Malmström, Eva
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Insights into the EDC-mediated PEGylation of cellulose nanofibrils and their colloidal stability2018Inngår i: Carbohydrate Polymers, ISSN 0144-8617, E-ISSN 1879-1344, Vol. 181, s. 871-878Artikkel i tidsskrift (Fagfellevurdert)
    Abstract [en]

    EDC-mediated coupling has frequently been utilized to poly(ethylene glycol) functionalize (PEGylate) cellulose-based materials, but no work has previously been reported on the direct N-(3-dimethylaminopropyl)-N-ethylcarbodiimide (EDC)-mediated PEGylation of cellulose nanofibrils (CNF). Herein, we report the first study where CNF has been directly sterically stabilized with amine-terminated PEG employing N-hydroxysuccinimide (NHS)-assisted EDC-coupling. This work has shown that this coupling reaction is highly sensitive to the reaction conditions and purification procedures, and hence an optimized coupling protocol was developed in order to achieve a reaction yield. Elemental analysis of the nitrogen content also showed the successful PEGylation. It was also shown that a surprisingly low PEGylation (1%) is sufficient to significantly improve the colloidal stability of the PEGylated samples, which reached dispersion-arrested-state-transitions at higher concentrations than neat CNF. The colloidal stability was preserved with increasing ionic strength, when comparably long polymer chains were grafted, targeting only 1% PEGylation.

  • 6.
    Kaldéus, Tahani
    et al.
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Nordenström, Malin
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Centra, Wallenberg Wood Science Center.
    Erlandsson, Johan
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Fiberteknologi.
    Wågberg, Lars
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Fiberteknologi.
    Malmström, Eva
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Redispersibility properties of dried cellulose nanofibrils - influence on structure and mechanical propertiesManuskript (preprint) (Annet vitenskapelig)
  • 7.
    Kaldéus, Tahani
    et al.
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Centra, Wallenberg Wood Science Center. KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Nordenström, Malin
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Fiberteknologi.
    Erlandsson, Johan
    Wågberg, Lars
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Fiberteknologi.
    Malmström, Eva
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Redispersibility properties of dried cellulose nanofibrils - influence on structure and mechanical properties2019Inngår i: Artikkel i tidsskrift (Annet vitenskapelig)
  • 8.
    Kaldéus, Tahani
    et al.
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Telaretti Leggieri, Maria Rosella
    Cobo Sanchez, Carmen
    Malmström, Eva
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    All-aqueous SI-ARGET ATRP from cellulose nanofibrils using hydrophilic and hydrophobic monomers2019Inngår i: Artikkel i tidsskrift (Annet vitenskapelig)
  • 9.
    Kaldéus, Tahani
    et al.
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Centra, Wallenberg Wood Science Center. KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Träger, Andrea
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Fiberteknologi.
    Berglund, Lars
    KTH, Skolan för teknikvetenskap (SCI), Farkost och flyg.
    Malmström, Eva
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    Lo Re, Giada
    Chalmers University of Technology.
    Molecular engineering of cellulose-PCL bio-nanocomposite interface by reactive amphiphilic copolymer nanoparticles2019Inngår i: Artikkel i tidsskrift (Fagfellevurdert)
  • 10.
    Kaldéus, Tahani
    et al.
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Centra, Wallenberg Wood Science Center.
    Träger, Andrea
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH).
    Berglund, Lars
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH).
    Malmström, Eva
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    Lo Re, Giada
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi, Biokompositer.
    Molecular Engineering of the Cellulose-Poly(Caprolactone) Bio-Nanocomposite Interface by Reactive Amphiphilic Copolymer Nanoparticles2019Inngår i: ACS NANO, Vol. 13, nr 6, s. 6409-6420Artikkel i tidsskrift (Fagfellevurdert)
    Abstract [en]

    A molecularly engineered water-borne reactive compatibilizer is designed for tuning of the interface in melt-processed thermoplastic poly(caprolactone) (PCL)-cellulose nanocomposites. The mechanical properties of the nanocomposites are studied by tensile testing and dynamic mechanical analysis. The reactive compatibilizer is a statistical copolymer of 2-(dimethylamino)ethyl methacrylate and 2-hydroxy methacrylate, which is subsequently esterified and quaternized. Quaternized ammonium groups in the reactive compatibilizer electrostatically match the negative surface charge of cellulose nanofibrils (CNFs). This results in core-shell CNFs with a thin uniform coating of the compatibilizer. This promotes the dispersion of CNFs in the PCL matrix, as concluded from high-resolution scanning electron microscopy and atomic force microscopy. Moreover, the compatibilizer "shell" has methacrylate functionalities, which allow for radical reactions during processing and links covalently with PCL. Compared to the bio-nanocomposite reference, the reactive compatibilizer (<4 wt %) increased Young's modulus by about 80% and work to fracture 10 times. Doubling the amount of peroxide caused further improved mechanical properties, in support of effects from higher cross-link density at the interface. Further studies of interfacial design in specific nanocellulose-based composite materials are warranted since the detrimental effects from CNFs agglomeration may have been underestimated.

  • 11.
    Larsson, Emma
    et al.
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Pendergraph, Samuel A.
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Kaldeus, Tahani
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Ytbehandlingsteknik. KTH, Skolan för kemivetenskap (CHE), Centra, Wallenberg Wood Science Center.
    Malmström, Eva
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Carlmark, Anna
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi, Ytbehandlingsteknik.
    Cellulose grafting by photoinduced controlled radical polymerisation2015Inngår i: Polymer Chemistry, ISSN 1759-9954, E-ISSN 1759-9962, Vol. 6, nr 10, s. 1865-1874Artikkel i tidsskrift (Fagfellevurdert)
    Abstract [en]

    The photoinduced controlled radical polymerisation (CRP) technique has been utilised to graft methyl acrylate (MA) and di(ethylene glycol) ethyl ether acrylate (DEGA) from filter paper. Grafting of MA was performed from alpha-bromoisobutyryl bromide functionalised papers. The amount of polymer grafted on the surface could be regulated by modifying the target DP of the reaction. SEC of cleaved linear polymer grafts showed that the grafting from filter papers proceeded with different kinetics compared to polymerisation from a free initiator added to the reaction mixture, resulting in higher dispersity. Furthermore, filter papers were polymerised with a-chloro-epsilon-caprolactone by surface-initiated ring opening polymerisation, yielding linear grafts containing initiating functions through-out the main chain. This functionality was subsequently utilised for the photoinduced CRP grafting of DEGA, yielding a graft-on-graft structure, which resulted in a thermoresponsive cellulose surface.

  • 12.
    Malmström, Eva
    et al.
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    Larsson, Emma
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    Kaldéus, Tahani
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi. KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Centra, Wallenberg Wood Science Center.
    Pendergraph, Samuel
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    Carlmark, Anna
    KTH, Skolan för kemi, bioteknologi och hälsa (CBH), Fiber- och polymerteknologi.
    Versatile modification of cellulose by UV-induced surface-initiated ATRP2015Inngår i: Abstracts of Papers of the American Chemical Society, ISSN 0065-7727, Vol. 249Artikkel i tidsskrift (Annet vitenskapelig)
  • 13.
    Mittal, Nitesh
    et al.
    KTH, Skolan för teknikvetenskap (SCI), Mekanik.
    Kaldéus, Tahani
    KTH, Skolan för kemivetenskap (CHE), Fiber- och polymerteknologi.
    Lundell, Fredrik
    KTH, Skolan för teknikvetenskap (SCI), Mekanik.
    Söderberg, Daniel
    KTH, Skolan för teknikvetenskap (SCI), Mekanik.
    Effect of cellulose nanofibril morphology on the strength and stiffness of macroscopic filaments2017Inngår i: Abstract of Papers of the American Chemical Society, ISSN 0065-7727, Vol. 253Artikkel i tidsskrift (Annet vitenskapelig)
1 - 13 of 13
RefereraExporteraLink til resultatlisten
Permanent link
Referera
Referensformat
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf