A synthesis protocol was identified to produce covalent grafting of poly(dimethyl siloxane) from cellulose, based on prior studies of analogous ring opening polymerizations. Following this polymer modification of cellulose, the contact adhesion was anticipated to be modified and varied as a function of the polymer molecular mass. The synthetic details were optimized for a filter paper surface before grafting the polymer from bulk cellulose spheres. The adhesion of the unmodified and grafted, bulk cellulose spheres were evaluated using the Johnson-Kendall-Roberts (JKR) theory with a custom build contact adhesion testing setup. We report the first example of grafting poly(dimethyl siloxane) directly from bulk cellulose using ring opening polymerization. For short grafting lengths, both the JKR work of adhesion and the adhesion energy at the critical energy release rate (G(c)) were comparable to unmodified cellulose beads. When polymer grafting lengths were extended sufficiently where chain entanglements occur, both the JKR work of adhesion and G(c) were increased by as much as 190%. Given the multitude of options available to graft polymers from cellulose, this study shows the potential to use this type of cellulose spheres to study the interaction between different polymer surfaces in a controlled manner. [GRAPHICS] .

this study the wet adhesion between Layer-by-Layer (LbL) assembled films of triblock copolymer micelles was investigated. Through the LbL assembly of triblock copolymer micelles with hydrophobic, low glass transition temperature (T-g) middle blocks and ionic outer blocks, a network of energy dissipating polymer chains with electrostatic interactions serving as crosslinks can be built. Four triblock copolymers were synthesized through Atom Transfer Radical Polymerisation (ATRP). One pair had a poly(2-ethyl-hexyl methacrylate) middle block with cationic or anionic outer blocks. The other pair contained the same ionic outer blocks but poly(n-butyl methacrylate) as the middle block. The wet adhesion was evaluated with colloidal probe AFM. To our knowledge, wet adhesion of the magnitude measured in this study has not previously been measured on any polymer system with this technique. We are convinced that this type of block copolymer system grants the ability to control the geometry and adhesive strength in a number of nano-and macroscale applications.

The photoinduced controlled radical polymerisation (CRP) technique has been utilised to graft methyl acrylate (MA) and di(ethylene glycol) ethyl ether acrylate (DEGA) from filter paper. Grafting of MA was performed from alpha-bromoisobutyryl bromide functionalised papers. The amount of polymer grafted on the surface could be regulated by modifying the target DP of the reaction. SEC of cleaved linear polymer grafts showed that the grafting from filter papers proceeded with different kinetics compared to polymerisation from a free initiator added to the reaction mixture, resulting in higher dispersity. Furthermore, filter papers were polymerised with a-chloro-epsilon-caprolactone by surface-initiated ring opening polymerisation, yielding linear grafts containing initiating functions through-out the main chain. This functionality was subsequently utilised for the photoinduced CRP grafting of DEGA, yielding a graft-on-graft structure, which resulted in a thermoresponsive cellulose surface.

The adhesive characteristics of poly(allylamine hydrochloride) (PAH)/hyaluronic acid (HA) self-assemblies were investigated using contact adhesion testing. Poly(dimethylsiloxane) spheres and silicon wafers were coated with layer-by-layer (LbL) assemblies of PAH/HA. NO increase in adhesion was observed when surfaces covered With dried LbL films were placed in contact. However, bringing the coated surfaces in contact while wet and separating them after drying resulted in an increase by a factor of 100 in the work of adhesion (from one to three bilayers). Herein we discuss the adhesion in PAH/HA and PAH/poly(acrylic acid) assemblies. PAH/HA assemblies have potential application as strong biomedical adhesives.