Hollandite ceramics are well-recognized as a promising host for immobilizing radioactive cesium. In the present paper, the [BaxCsy][(Al3+,Ti3+)(2x +y)Ti-8-2x-y(4+)]O-16 (0.4 <= x, y <= 0.8) ceramics were fabricated to in-vestigate the effect of incorporated Cs on structural stability and durability of (Ba,Cs)(Al,Ti)(8)O-16 ceramics with Cs-incorporated. It was found that the sintered samples at 1250 degrees C show a pure hollandite phase with tetragonal structure (I4/m) and high Cs retention. Moreover, the synthesized (Ba,Cs)(Al,Ti)(8)O-16 ceramics exhibit an excellent aqueous stability and the normalized Cs release rate is 2.82 (+/- 0.27) x10(-3) g m(-2) d(-1) after 28 days. All these results reveal that (Ba,Cs)(Al,Ti)(8)O-16 is a promising candidate as a Cs-waste form.