Four TiAl alloys with different Mo contents were designed, and the microstructure and mechanical properties of these MoTiAl alloys were studied by scanning electron microscope, nanoindentation, and hot compression simulation methods. Results show that with increasing the Mo content, the content of. phase is gradually decreased, while that of beta phase is gradually increased. The Mo element mainly exists in the form of beta phase in the TiAl alloy. During the hot isostatic pressing process, the Mo element is diffused from the. and a 2 phases to the beta phase. The nanoindentation hardness of Mo-TiAl alloy reaches the maximum when the Mo content is 1.59at%, and it is negatively correlated with the interlamellar space. As the content of Mo element increases, the flow stress of Mo-TiAl alloys decreases, and the TiAl alloys with 2.11at% and 3.94at% Mo addtion have poor plasticity due to the Al element segregation.