Polyacrylonitrile (PAN) nanofibers functionalized with amine groups (PAN-NH2) were prepared using a simple one-step reaction route. The PAN-NH2 nanofibers were investigated for the removal of chromium(VI) from aqueous solutions. The adsorption and the kinetic characteristics were evaluated in batch process. The adsorption process showed pH dependence and the maximum Cr(VI) adsorption occurred at pH = 2. The Langmuir adsorption model described well the experimental adsorption data and estimated a maximum loading capacity of 156 mg/g, which is a markedly high value compared to other adsorbents reported. The kinetics studies indicated that the equilibrium was attained after 90 min and the experimental data followed a pseudo-second order model suggesting a chemisorption process as the rate limiting step. X-ray Photoelectron Spectroscopy (XPS) and Fourier transform infrared spectroscopy (FT-IR) revealed that the adsorption of Cr(VI) species on PAN-NH2 was facilitated through both electrostatic attraction and surface complexation. High desorption efficiency (> 90%) of Cr(VI) was achieved using diluted base solutions that may allow the reuse of PAN-NH2 nanofibers.

Chromium (Cr) in the form of Cr(VI) is deemed toxic in water due to its mutagenic and carcinogenic properties. For the successful removal of Cr(VI), we demonstrate a novel adsorbent consisting of superparamagnetic iron oxide nanoparticles (SPION) functionalized with 3-Mercaptopropionic acid (3-MPA). Fourier transform infrared spectroscopy (FT-IR) confirmed the functionalization of nanoparticles and presence of sulfonate groups. Batch adsorption experiments showed that the functionalized adsorbent recovered 45 mg of Cr(VI)/g of 3-MPA coated SPION at initial concentration of 50 mg/L aqueous solution at pH 1 with less than 1% of Fe dissolution from SPION. The results from X-ray photoelectron spectroscopy confirmed that Cr(VI) chemisorbed onto the adsorbent. Hence, the XPS spectra did not indicate any reduction of Cr(VI) to Cr(III) upon adsorption. The adsorption data were better fitted for the Freundlich model. Moreover, the Cr(VI) adsorption kinetics on functionalized SPION followed a pseudo-second order rate, revealing chemisorption as the dominant mechanism. The high Cr(VI) removal, rapid adsorption kinetics and stability of adsorbent indicate that 3-MPA coated SPION could be an efficient adsorbent for the removal of Cr(VI).

This study describes the removal of Chromium(VI) from aqueous solutions using surface tailored superparamagnetic iron oxide nanoparticles (SPION) coated with bis(2,4,4-trimethylpentyl)dithiophosphinic acid (Cyanex-301). The synthesized Cyanex-301 coated SPION has been characterized by Transmission Electron Microscopy (TEM), Fourier-Transfer Infrared Spectroscopy (FT-IR), X-ray Photonic Spectroscopy (XPS), and Thermogravimetric Analysis (TGA). The adsorption mechanism was proposed to be via complexation between the thiol group on Cyanex-301 and Cr(VI) ions based on the XPS and FTIR analysis. It has been found that the equilibrium can be attained in less than 2hr. The adsorption behavior of Cr(VI) on the Cyanex-301 coated SPION can be well described by the Langmuir model and the maximum adsorption capacity for Cr(VI) was estimated to be 30.8mg/g. The selectivity of the Cyanex-301 coated SPION adsorbent towards Cr(VI) ions was found to be high and the maximum loading capacity obtained is up to an order of magnitude higher than that of other adsorbents reported in the literature. The desorption studies showed that more than 70% of Cr(VI) can be recovered using HNO3 as eluting solution. Our findings suggest a high potential of the designed adsorbent material for the treatment of industrial wastewater containing Cr(VI).

Microsomal glutathione transferase 1 (MGST1) is an antioxidant enzyme located predominantly in the mitochondrial er membrane and endoplasmk reticulum and has been shown to protect cells from lipid peroxidation induced by a variety of cytostatic drugs and pro-oxidant stimuli. We hypothesized that MGST1 may also protect against nanomaterial-induced cytotoxicity through a specific effect on lipid peroxidation. We evaluated the induction of cytotoxicity and oxidative stress by TiO2, CeO2, SiO2, and ZnO in the human MCF-7 cell line with or without overexpression of MGST1. SiO2 and ZnO nanoparticles caused dose- and time-dependent toxicity, whereas no obvious cytotoxic effects were induced by nanoparticles of TiO2 and CeO2. We also noted pronounced cytotoxicity for three out of four additional SiO2 nanoparticles tested. Overexpression of MGST1 reversed the cytotoxicity of the main SiO2 nanoparticles tested and for one of the supplementary SiO2 nanoparticles but did not protect cells against ZnO-induced cytotoxic effects. The data point toward a role of lipid peroxidation In SiO2 nanoparticle-induced cell death. For ZnO nanoparticles, rapid dissolution was observed, and the subsequent interaction of Zn2+ with cellular targets is likely to contribute to the cytotoxic effects. A direct inhibition of MGST1 by Zn2+ could provide a possible explanation for the lack of protection against ZnO nanoparticles in this model. Our data also showed that SiO2 nanoparticle-induced cytotoxicity is mitigated in the presence of serum, potentially through masking of reactive surface groups by serum proteins, whereas ZnO nanoparticles were cytotoxic both In the presence and in the absence of serum.

A number of commercially available metal/metal oxide nanoparticles (NPs) such as superparamagnetic iron oxide (SPION) are utilized by the medical field for a wide variety of applications. These NPs may able to induce dermal toxicity via their physical nature and reactive surface properties. We hypothesize that SPION may be toxic to skin via the ability of particles to be internalized and thereby initiate oxidative stress, inducing redox-sensitive transcription factors affecting/leading to inflammation. Due to the skin's susceptibility to UV radiation, it is also of importance to address the combined effect of UVB and NPs co-exposure. To test this hypothesis, the effects of dextran-coated SPION of different sizes (15-50 nm) and manufacturers (MicroMod, Rostock-Warnemunde, Germany and KTH-Royal Institute of Technology, Stockholm, Sweden) were evaluated in two cell lines: normal human epidermal keratinocytes (HEK) and murine epidermal cells (JB6 P+). HEK cells exposed to 20 nm (KTH and MicroMod) had a decrease in viability, while the 15 and 50 nm particles were not cytotoxic. HEK cells were also capable of internalizing the KTH particles (15 and 20 nm) but not the MicroMod SPION (20 and 50 nm). IL-8 and IL-6 were also elevated in HEK cells following exposure to SPION. Exposure of JB6 P+ cells to all SPIONs evaluated resulted in activation of AP-1. Exposure to SPION alone was not sufficient to induce NF-kappa B activation; however, co-exposure with UVB resulted in significant NF-kappa B induction in cells exposed to 15 and 20 nm KTH SPION and 50 nm MicroMod particles. Pre-exposure of JB6 P+ cells to UVB followed by NPs induced a significant depletion of glutathione, release of cytokines, and cell damage as assessed by release of lactate dehydrogenase. Altogether, these data indicate that co-exposure to UVB and SPIONs was associated with induction of oxidative stress and release of inflammatory mediators. These results verify the need to thoroughly evaluate the adverse effects of UVB when evaluating dermal toxicity of engineered NPs on skin.

Nanomaterials of ZnO-PLLA nanofibers have been used for the adsorption of Cr(VI) as a prime step for the purification of water.The fabrication and application of the flexible ZnO-PLLA nanofiber nanocomposite as functional materials in this well-developedarchitecture have been achieved by growing ZnO nanorod arrays by chemical bath deposition on synthesized electrospun poly-Llactidenanofibers. The nanocomposite material has been tested for the removal and regeneration of Cr(IV) in aqueous solutionunder a “continuous flow mode” by studying the effects of pH, contact time, and desorption steps.Theadsorption of Cr(VI) speciesin solution was greatly dependent upon pH. SEM micrographs confirmed the successful fabrication of the ZnO-PLLA nanofibernanocomposite.Theadsorption and desorption of Cr(VI) species were more likely due to the electrostatic interaction between ZnOand Cr(VI) ions as a function of pH.The adsorption and desorption experiments utilizing the ZnO-PLLAnanofiber nanocompositehave appeared to be an effective nanocomposite in the removal and regeneration of Cr(VI) species.